QTS PLA-Flavor Black Tea Matte Filament (1.75mm) - Infused with Natural Taiwan Black Tea Fiber | Elegant Matte Finish & Warm Aroma | 1KG
Infuse your 3D prints with the warmth and elegance of QTS PLA-Flavor Black Tea. This premium 1.75mm filament is infused with recycled natural black tea fibers from Taiwan's renowned tea estates. It delivers a sophisticated, deep matte finish with a warm, earthy tone that beautifully conceals layer lines. During printing, it releases a subtle, comforting black tea fragrance, making it the perfect choice for vintage-style decor, wood-like prototypes, and high-end artistic creations.
QTS PLA-Flavor Black Tea — Timeless Elegance & Organic Texture
Infuse your creations with the warmth and sophistication of QTS PLA-Flavor Black Tea. Crafted using recycled natural fibers from Taiwan's premium black tea production, this filament offers a deep, earthy red-brown matte finish. It provides a rich, organic texture that moves away from the artificial look of plastic, making it perfect for classic and contemporary designs alike.
Why QTS Outperforms Competitors?
Advanced Light Scattering: Our high-density tea fiber composite naturally scatters light across the surface, making layer lines nearly invisible and providing a professional "injection-molded" look.
Bambu Lab Optimized: Engineered for high-speed stability, supporting printing speeds up to 300mm/s while maintaining superior layer adhesion and surface consistency.
Sustainable Innovation: We transform Taiwan's agricultural heritage into high-performance materials, offering a truly eco-friendly alternative to standard PLA.
Key Advantages
- ✔Elegant Printing Atmosphere: Releases a comforting black tea fragrance during the printing process (odorless after cooling).
- ✔Deep Matte Finish: A non-reflective, sophisticated surface that excels in any lighting condition.
- ✔High-Speed Performance: Optimized for modern high-speed motion systems without sacrificing detail.
- ✔Easy Post-Processing: The fiber-filled nature makes it exceptionally easy to sand for a wood-like finish.
Applications & Use Cases
Technical Specifications & Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength (X-Y) | 45.2 Mpa |
| Tensile Modulus (X-Y) | 1810 Mpa |
| Elongation at Break | 4.70% |
| Bending Strength (X-Y) | 74 Mpa |
| Flexural Modulus (X-Y) | 2920 Mpa |
| Impact Strength (X-Y) | 29.72 KJ/m2 |
| Heat Distortion Temp | 60°C (0.45MPa) |
| Melt Flow Index | 30~35 g/10min (210°C, 2.16kg) |
| Printing Temp / Speed | 190°C - 230°C / 150 - 300 mm/s |
How to Use - Best Practices
For the best results, we recommend a printing temperature of 215°C and a bed temperature of 60°C. A hardened steel nozzle is recommended for long-term use. To maintain the deep matte finish, ensure the filament is stored in a dry environment.
Printer Compatibility
Fully compatible with all open-source FDM printers, including Bambu Lab (X1/P1/A1), Creality, Prusa, and Anycubic. Optimized for high-speed motion systems.
Frequently Asked Questions (FAQ)
Q: Does the final print smell like tea? A: The soothing aroma is a unique feature during the printing process. Once cooled, the final object is odorless.
Q: Can I sand this material? A: Yes, the fiber content makes it very easy to sand, allowing for a smooth, organic finish.
Customer Success Stories
"The Black Tea PLA has a richness that I haven't found in other filaments. It looks like aged wood once it's printed. My customers love the subtle scent and the sophisticated matte finish." — Artisan Maker, New York
Safety & Storage
Store in a cool, dry place using the included resealable bag and desiccant. RoHS and REACH compliant for a safer printing experience.